AbstractsChemistry

Anodic tin oxide films: fundamentals and applications

by Anna Palacios Padrós




Institution: Universitat de Barcelona
Department:
Year: 2015
Keywords: Estany; Estaño; Tin; Òxids metàl·lics; Oxidos metálicos; Metallic oxides; Detectors de gasos; Detectores de gases; Gas detectors; Fotoquímica; Photochemistry; Anodització; Anodización; Anodizing; Ciències Experimentals i Matemàtiques
Record ID: 1126400
Full text PDF: http://hdl.handle.net/10803/292727


Abstract

The study of the electrochemical oxidation behaviour of tin in alkaline media, the development of anodic self-ordered tin oxide nanostructures and its application to laboratory scale devices have been the main focus of this PhD Thesis. The passivation process of Sn has been studied from an electrochemical approach covering the whole range from hydrogen evolution to the final passivation of the metal. The oxides formed in each relevant potential region have been characterized by ex situ techniques and a mechanism for the process has been proposed by correlating composition, morphology and electronic properties. Three main processes have been identified: the formation of a SnO·nH2O primary passive layer; the hydroxyl induced etching of tin and concurrent SnO precipitation; and the final passivation due to the growth of Sn(IV) based oxides. Also, in situ techniques like EC-STM were used to gain more knowledge on the growth mechanism, especially for the first oxidation process. Before the onset of the peak, the formation of islands and metal dissolution and redeposition phenomena were observed. The composition of these islands is still under study. The knowledge gained while attaining this first goal is used for the design of protocols to develop self-ordered anodic tin oxide structures. In this view, several electrolytes were explored to find one that allows growing self-ordered tin oxide structures without the actual limitations of the films prepared in oxalic acid or NaOH: clogged pores and cracks on its cross-section. Once proper structures were attained in the new Na2S and NH4F electrolyte, applications such as gas sensing or photoelectrochemical water splitting were attempted in order to assess their value. The as-grown nanochannelled tin oxide structures are in general amorphous so an appropriate thermal treatment is required to convert them into SnO2, which is a material commonly applied in hydrogen sensors. Our layers proved to have superior characteristics by detecting H2 concentrations as low as 9 ppm and by operating at relatively low temperatures (80 ºC). The performance is comparable to that of noble-metal doped SnO2 particles or single SnO2 nanowires and superior to that of other self-ordered structures prepared in non-optimized conditions or oxalic acid. The opening of the pores provides a higher specific area whereas the continuity of the channels improves the conducting properties and the transference of electrons through the structure. By adjusting the annealing conditions, SnO2 nanochannelled structures with absorption in the visible range were prepared. A band gap of 2.4 eV was achieved for self-ordered tin oxide structures annealed at 200 ºC in Argon atmosphere due to the improved crystallinity, with respect to as-grown samples, together with the conservation of the Sn2+ defects and oxygen vacancies. These layers could have potential applications in photoelectrochemical water splitting or photocatalysis. Despite the enhancement in collecting visible light, the structures were found to be…