Abstracts Chemistry

Corrosion Inhibition Performance of Imidazolium IonicLiquids and Their Influence On Surface Ferrous Carbonate LayerFormation

by Dongrui Yang

Corrosion inhibitors as effective anti-corrosion applications were widely studied and drawn much attention in both academe and industrial area. In this work, a systematic work, including inhibitors selection, anti-corrosion property and characterization, influence on scale formation, testing system design and so on, were reported. The corrosion inhibition performance of four imidazolium ionic liquids in carbon dioxide saturated NaCl solution was investigated by using electrochemical and surface analysis technologies. The four compounds are 1-ethyl-3-methylimidazolium chloride (a), 1-butyl-3-methylimidazolium chloride (b), 1-hexyl-3-methylimidazolium chloride (c), 1-decyl-3-methylimidazolium chloride (d). Under the testing conditions, compound d showed the highest inhibition efficiency and selected as the main object of further study.As a selected representative formula, 1-decyl-3-methylimidazolium chloride was studied in detail about its corrosion inhibition performance on mild steel in carbon dioxide saturated NaCl brine at pH 3.8 and 6.8. Electrochemical and surface analysis techniques were used to characterize the specimen corrosion process during the immersion in the blank and inhibiting solutions. The precorrosion of specimen surface showed significant and different influences on the anti-corrosion property of DMICL at pH 3.8 and 6.8. The corrosion inhibition efficiency (IE) was calculated based on parameters obtained from electrochemical techniques; the achieved IE was higher than 98% at the 25th hour for the steel with a well-polished surface at pH 3.8. The fitting parameters obtained from electrochemical data helped to account for the interfacial changes.As proved in previous research, 1-decyl-3-methylimidazolium chloride could be used as good corrosion inhibitors under certain conditions. However, under other conditions, such chemicals, as well as other species in oil transporting system, could be a factor influencing the evolution of protective surface inorganic layer. In this part, the FeCO3 layer evolution process for API 5L X52 carbon steel in CO2-saturated NaCl brine in the absence and in the presence of 1-decyl-3-methylimidazolium chloride ionic liquid was characterized using electrochemical techniques. Two models were developed to account for the interfacial evolution: the first model considered the balance of positive and negative charges at the interface of the metal and electrolyte in blank solution, while the second one considered the layer coverage and evolution with the imidazolium compound.The corrosion testing system is scientifically and practically critical for corrosion testing and simulations. In this part, a flowing fluid loop cell (FFLC) system was constructed to simulate the corrosion environment in the pipeline. Main content of this work include the construction of the flowing fluid cell loop (FFLC) system, as well as FFLC-based corrosion/anticorrosion tests under simulated acid conditions. Electrochemical Impedance Spectroscopy (EIS) and Linear Polarization Resistance (LPR) were used… Advisors/Committee Members: Cong , Hongbo (Committee Chair), Castaneda , Homero (Advisor).