Abstracts Category : Other

Aerosol Combustion Synthesis of Nanopowders and Processing to Functional Thin Films

by Eongyu Yi

In this dissertation, the advantages of liquid-feed flame spray pyrolysis (LF-FSP) process in producing nanoparticles (NPs) as well as processing the produced NPs to ceramic/polymer nanocomposite films and high density polycrystalline ceramic films are demonstrated. The LF-FSP process aerosolizes alcohol solutions of metalloorganic precursors by oxygen and combusts them at > 1500 C. The combustion products are rapidly quenched (~10s of ms) to < 400 C, producing NPs with the same compositions as those of the precursor solutions. The high specific surface areas of NPs enable formulation of ceramic/polymer/interface(phase) ternary nanocomposites in which the interphase can be the determining factor of the final net properties. In ceramic processing, NPs show increased sinterability and provide access to small average grain sizes with fine control of microstructures, compared to when micron sized powders are used. Therefore, synthesis, processing, and characterization of NPs, NP derived nanocomposites and ceramic monoliths are of great interest.We first compare the LF-FSP to commercial FSP process by producing fumed silica. Combusting spirocyclic alkoxysilanes or Si(OEt)4 by LF-FSP process produced fumed silica very similar to SiCl4 derived products. Given LF-FSP approach does not require the containment constraints of the SiCl4 process and precursors are synthesized from rice hull ash, the reported approach represents a sustainable, green and potentially lower cost alternative.We then show the versatility of NPs in formulating flexible ceramic/polymer nanocomposites (BaTiO3/epoxy) with superior properties. Volume fractions of the BaTiO3 filler and composite film thicknesses were controlled to adjust the net dielectric constant and the capacitance. Measured net dielectric constants further deviated from theory, with increasing solids loadings, due to NP agglomeration. Wound nanocomposite capacitors showed ten times higher capacitance compared to the commercial counterpart.Following series of studies explore the use of flame made NPs in processing Li+ conducting membranes. Systematic doping studies were conducted in the LiTi2(PO4)3 system to modify the lattice constant, conduction channel width, and sintering behavior by introducing Al3+ and Si4+ dopants. Excess Li2O content was also adjusted to observe its effect on final microstructures and phase compositions. Improved densification rates were found in Li1.7Al0.3Ti1.7Si0.4P2.6O12 composition and thin films (521 m) with conductivities of 0.3-0.5 mS cm-1 were achieved. Li6.25M0.25La3Zr2O12 (M = Al3+, Ga3+) thin films (25-28 m) with conductivities of 0.2-1.3 mS cm-1 were also successfully processed using flame made NPs, overcoming processing challenges extant, resulting in significantly reduced energy input required for densification. Heating schedules, sintering atmospheres, and types of substrates were controlled to observe their effect on the sintering behavior. Furthermore, green film thicknesses were found to be a crucial variable determining the finalAdvisors/Committee Members: Laine, Richard M (committee member), Thompson, Levi Theodore (committee member), Heron, John Thomas (committee member), Kieffer, John (committee member).